Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 4432 15Cr3-S (IS 4432:1988) and IS 1570 (Part 7) 10Mo6H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
IS 4432 15Cr3-S is typically used for forgings and fabrication of case-hardened machine or automobile parts, while IS 1570 (Part 7) 10Mo6H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
IS 4432 15Cr3-S is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 10Mo6H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 4432 15Cr3-S vs IS 1570 (Part 7) 10Mo6H is a 65.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4432 15Cr3-S
IS 1570 (Part 7) 10Mo6H
Core Tensile Strength
650-900 MPa (16 mm) / 600-900 MPa (30 mm)
Not specified
Core Yield Strength
>=430 MPa (16 mm) / >=360 MPa (30 mm)
Not specified
Core Elongation
>=12% (16 mm) / >=14% (30 mm)
Not specified
Core Reduction of Area
>=35% (16 mm) / >=40% (30 mm)
Not specified
Hardness, annealed (A)
<=174 HB
Not specified
Tensile Strength
Not specified
>=415 MPa
Yield Strength
Not specified
>=205 MPa (0.2 % proof stress)
Elongation
Not specified
>=30%
Condition
Not specified
Tubes, N+T, thickness - (first row of Table 3)
Typical Applications
IS 4432 15Cr3-S
Forgings and fabrication of case-hardened machine or automobile parts
IS 1570 (Part 7) 10Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 10Mo6H specifies Mo which is not specified for IS 4432 15Cr3-S.
Can IS 4432 15Cr3-S Be Substituted With IS 1570 (Part 7) 10Mo6H?
IS 4432 15Cr3-S and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 4432 15Cr3-S and IS 1570 (Part 7) 10Mo6H?
IS 1570 (Part 7) 10Mo6H specifies Mo which is not specified for IS 4432 15Cr3-S.
Can IS 4432 15Cr3-S be substituted with IS 1570 (Part 7) 10Mo6H?
IS 4432 15Cr3-S and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.