IS 4432 15Ni7Cr4Mo2-S vs IS 1570 (Part 4) 15Ni7Cr4Mo2

Close Alternative — 81.4% match based on chemical composition and mechanical property overlap.

IS 4432 15Ni7Cr4Mo2-S (IS 4432:1988) and IS 1570 (Part 4) 15Ni7Cr4Mo2 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 4432 15Ni7Cr4Mo2-S is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 15Ni7Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4432 15Ni7Cr4Mo2-S vs IS 1570 (Part 4) 15Ni7Cr4Mo2 is a 97.1% match. As per mechanical properties, the match is 50%. Combined, this makes them a close alternative overall at 81.4%.

Frequently Compared With IS 4432 15Ni7Cr4Mo2-S:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
97.1%
MECHANICAL MATCH
50%
OVERALL
81.4%
Specifications
Property IS 4432 15Ni7Cr4Mo2-S IS 1570 (Part 4) 15Ni7Cr4Mo2
Standard IS 4432:1988 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Si (%) 0.15-0.35 0.15-0.35
Mn (%) 0.60-1.00 0.60-1.00
Ni (%) 1.50-2.00 1.50-2.00
Cr (%) 0.75-1.25 0.75-1.25
Mo (%) 0.10-0.20 0.10-0.20
S (%) 0.020-0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4432 15Ni7Cr4Mo2-S IS 1570 (Part 4) 15Ni7Cr4Mo2
Core Tensile Strength 1100-1400 MPa (16 mm) / 1050-1400 MPa (30 mm) / 800-1100 MPa (63 mm) Not specified
Core Yield Strength >=750 MPa (16 mm) / >=730 MPa (30 mm) / >=550 MPa (63 mm) Not specified
Core Elongation >=9% (16 mm) / >=10% (30 mm) / >=12% (63 mm) Not specified
Core Reduction of Area >=40% (16 mm) / >=40% (30 mm) / >=45% (63 mm) Not specified
Hardness, annealed (A) <=229 HB Not specified
Tensile Strength Not specified >=1080 MPa
Elongation Not specified >=9%
Izod Impact Not specified >=35 J
Condition Not specified Case hardening steel, refined and quenched, core properties
Typical Applications
IS 4432 15Ni7Cr4Mo2-S
Forgings and fabrication of case-hardened machine or automobile parts
IS 1570 (Part 4) 15Ni7Cr4Mo2
Not documented
Key Differences
Can IS 4432 15Ni7Cr4Mo2-S Be Substituted With IS 1570 (Part 4) 15Ni7Cr4Mo2?
IS 4432 15Ni7Cr4Mo2-S and IS 1570 (Part 4) 15Ni7Cr4Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 4432 15Ni7Cr4Mo2-S
0 active listings and RFQs →
IS 1570 (Part 4) 15Ni7Cr4Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4432 15Ni7Cr4Mo2-S and IS 1570 (Part 4) 15Ni7Cr4Mo2?
IS 4432 15Ni7Cr4Mo2-S specifies S, P which are not specified for IS 1570 (Part 4) 15Ni7Cr4Mo2.
Can IS 4432 15Ni7Cr4Mo2-S be substituted with IS 1570 (Part 4) 15Ni7Cr4Mo2?
IS 4432 15Ni7Cr4Mo2-S and IS 1570 (Part 4) 15Ni7Cr4Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.