IS 4432 16Ni3Cr2 vs UNI 11234 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 4432 16Ni3Cr2 (IS 4432:1988) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. IS 4432 16Ni3Cr2 is typically used for forgings and fabrication of case-hardened machine or automobile parts, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. IS 4432 16Ni3Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, IS 4432 16Ni3Cr2 vs UNI 11234 100Cr6 is a 66.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 4432 16Ni3Cr2:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H
Match Breakdown
CHEMISTRY MATCH
66.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 4432 16Ni3Cr2 UNI 11234 100Cr6
Standard IS 4432:1988 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.12-0.20 0.93-1.05
Si (%) 0.15-0.35 0.15-0.35
Mn (%) 0.60-1.00 0.25-0.45
Ni (%) 0.60-1.00 Not specified
Cr (%) 0.40-0.80 1.35-1.65
S (%) <=0.035 <=0.025
P (%) <=0.035 <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4432 16Ni3Cr2 UNI 11234 100Cr6
Core Tensile Strength 1100-1400 MPa (16 mm) / 1050-1400 MPa (30 mm) / 900-1200 MPa (63 mm) Not specified
Core Yield Strength >=750 MPa (16 mm) / >=720 MPa (30 mm) / >=600 MPa (63 mm) Not specified
Core Elongation >=8% (16 mm) / >=9% (30 mm) / >=11% (63 mm) Not specified
Core Reduction of Area >=35% (16 mm) / >=40% (30 mm) / >=45% (63 mm) Not specified
Hardness, annealed (A) <=207 HB Not specified
Tensile Strength Not specified 750-1000 MPa
Yield Strength Not specified 400-600 MPa
Elongation Not specified 10-14 %
Hardness Not specified 60-64 HRC
Typical Applications
IS 4432 16Ni3Cr2
Forgings and fabrication of case-hardened machine or automobile parts
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can IS 4432 16Ni3Cr2 Be Substituted With UNI 11234 100Cr6?
IS 4432 16Ni3Cr2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 4432 16Ni3Cr2
No active listings currently.
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
IS 4432 16Ni3Cr2
0 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4432 16Ni3Cr2 and UNI 11234 100Cr6?
IS 4432 16Ni3Cr2 specifies Ni which is not specified for UNI 11234 100Cr6.
Can IS 4432 16Ni3Cr2 be substituted with UNI 11234 100Cr6?
IS 4432 16Ni3Cr2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.