IS 4432 20Ni7Cr2Mo2-S vs SAE J404 4320

Strong Match — 97.8% match based on chemical composition and mechanical property overlap.

IS 4432 20Ni7Cr2Mo2-S (IS 4432:1988) and SAE J404 4320 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. IS 4432 20Ni7Cr2Mo2-S is typically used for forgings and fabrication of case-hardened machine or automobile parts, while SAE J404 4320 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. IS 4432 20Ni7Cr2Mo2-S is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 4320 is defined under SAE International, originating from United States.

As per chemical composition, IS 4432 20Ni7Cr2Mo2-S vs SAE J404 4320 is a 97.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 97.8%.

Frequently Compared With IS 4432 20Ni7Cr2Mo2-S:
IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H UNI 11234 100Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
97.8%
MECHANICAL MATCH
No shared data
OVERALL
97.8%
Specifications
Property IS 4432 20Ni7Cr2Mo2-S SAE J404 4320
Standard IS 4432:1988 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.17-0.22 0.17-0.22
Si (%) 0.15-0.35 0.15-0.35
Mn (%) 0.45-0.65 0.45-0.65
Ni (%) 1.65-2.00 1.65-2.00
Cr (%) 0.40-0.60 0.40-0.60
Mo (%) 0.20-0.30 0.20-0.30
S (%) 0.020-0.035 <=0.040
P (%) <=0.035 <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4432 20Ni7Cr2Mo2-S SAE J404 4320
Core Tensile Strength 950-1350 MPa (16 mm) / 850-1200 MPa (30 mm) / 800-1150 MPa (63 mm) Not specified
Core Yield Strength >=650 MPa (16 mm) / >=600 MPa (30 mm) / >=550 MPa (63 mm) Not specified
Core Elongation >=8% (16 mm) / >=9% (30 mm) / >=10% (63 mm) Not specified
Core Reduction of Area >=35% (16 mm) / >=35% (30 mm) / >=40% (63 mm) Not specified
Hardness, annealed (A) <=229 HB Not specified
Typical Applications
IS 4432 20Ni7Cr2Mo2-S
Forgings and fabrication of case-hardened machine or automobile parts
SAE J404 4320
Chemistry-only alloy steel grade; see the composition notes for product scope
Can IS 4432 20Ni7Cr2Mo2-S Be Substituted With SAE J404 4320?
IS 4432 20Ni7Cr2Mo2-S and SAE J404 4320 overlap closely enough on chemistry and mechanical properties that SAE J404 4320 is often considered as a substitute for IS 4432 20Ni7Cr2Mo2-S in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 4432 20Ni7Cr2Mo2-S
0 active listings and RFQs →
SAE J404 4320
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4432 20Ni7Cr2Mo2-S and SAE J404 4320?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4432 20Ni7Cr2Mo2-S be substituted with SAE J404 4320?
IS 4432 20Ni7Cr2Mo2-S and SAE J404 4320 overlap closely enough on chemistry and mechanical properties that SAE J404 4320 is often considered as a substitute for IS 4432 20Ni7Cr2Mo2-S in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.