IS 5517 15Cr13Mo6 vs SAE J404 4130

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 5517 15Cr13Mo6 (IS 5517:1993) and SAE J404 4130 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. IS 5517 15Cr13Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 4130 is defined under SAE International, originating from United States.

As per chemical composition, IS 5517 15Cr13Mo6 vs SAE J404 4130 is a 70.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 5517 15Cr13Mo6:
NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 UNI 11234 100Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H IS 4367 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
70.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 5517 15Cr13Mo6 SAE J404 4130
Standard IS 5517:1993 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.10-0.20 0.28-0.33
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.40-0.70 0.40-0.60
Cr (%) 2.90-3.40 0.80-1.10
Mo (%) 0.45-0.65 0.15-0.25
S (%) <=0.035 <=0.040
P (%) <=0.035 <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 15Cr13Mo6 SAE J404 4130
Tensile Strength 700-850 MPa Not specified
Yield Strength (0.2% proof) 540 MPa min Not specified
Elongation >=18% Not specified
Izod Impact 55 J min Not specified
Hardness (annealed) <=200 HB Not specified
Condition Hardened and tempered, ruling section up to 150 mm Not specified
Typical Applications
IS 5517 15Cr13Mo6
Not documented
SAE J404 4130
Aircraft structures, pressure vessels, high tensile tubes
Can IS 5517 15Cr13Mo6 Be Substituted With SAE J404 4130?
IS 5517 15Cr13Mo6 and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 5517 15Cr13Mo6
No active listings currently.
SAE J404 4130
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6400 mm (224.41–251.97 in)
On M-EX Right Now
IS 5517 15Cr13Mo6
0 active listings and RFQs →
SAE J404 4130
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 15Cr13Mo6 and SAE J404 4130?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5517 15Cr13Mo6 be substituted with SAE J404 4130?
IS 5517 15Cr13Mo6 and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.