IS 5517 30C8 vs BS 970 (Part 3) 080A30

Strong Match — 93.7% match based on chemical composition and mechanical property overlap.

IS 5517 30C8 (IS 5517:1993) and BS 970 (Part 3) 080A30 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. IS 5517 30C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 080A30 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 5517 30C8 vs BS 970 (Part 3) 080A30 is a 93.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.7%.

Frequently Compared With IS 5517 30C8:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10
Match Breakdown
CHEMISTRY MATCH
93.7%
MECHANICAL MATCH
No shared data
OVERALL
93.7%
Specifications
Property IS 5517 30C8 BS 970 (Part 3) 080A30
Standard IS 5517:1993 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.25-0.35 0.26-0.34
Si (%) 0.10-0.35 0.10-0.40
Mn (%) 0.60-0.90 0.70-0.90
S (%) <=0.035 <=0.05
P (%) <=0.035 <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 30C8 BS 970 (Part 3) 080A30
Tensile Strength 600-750 MPa Not specified
Yield Strength (0.2% proof) 400 MPa min Not specified
Elongation >=18% Not specified
Izod Impact 55 J min Not specified
Hardness (annealed) <=187 HB Not specified
Condition Hardened and tempered, ruling section up to 30 mm Not specified
Typical Applications
IS 5517 30C8
Not documented
BS 970 (Part 3) 080A30
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; carbon and carbon manganese steel (Table 13)
Can IS 5517 30C8 Be Substituted With BS 970 (Part 3) 080A30?
IS 5517 30C8 and BS 970 (Part 3) 080A30 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080A30 is often considered as a substitute for IS 5517 30C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 5517 30C8
0 active listings and RFQs →
BS 970 (Part 3) 080A30
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 30C8 and BS 970 (Part 3) 080A30?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5517 30C8 be substituted with BS 970 (Part 3) 080A30?
IS 5517 30C8 and BS 970 (Part 3) 080A30 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080A30 is often considered as a substitute for IS 5517 30C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.