IS 5517 30Ni13Cr5 vs IS 1570 (Part 4) 30Ni16Cr5

Close Alternative — 72.4% match based on chemical composition and mechanical property overlap.

IS 5517 30Ni13Cr5 (IS 5517:1993) and IS 1570 (Part 4) 30Ni16Cr5 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 5517 30Ni13Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 30Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 5517 30Ni13Cr5 vs IS 1570 (Part 4) 30Ni16Cr5 is a 96.1% match. As per mechanical properties, the match is 25%. Combined, this makes them a close alternative overall at 72.4%.

Frequently Compared With IS 5517 30Ni13Cr5:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
96.1%
MECHANICAL MATCH
25%
OVERALL
72.4%
Specifications
Property IS 5517 30Ni13Cr5 IS 1570 (Part 4) 30Ni16Cr5
Standard IS 5517:1993 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.26-0.34 0.26-0.34
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 3.90-4.30 3.90-4.30
Cr (%) 1.00-1.40 1.10-1.40
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 30Ni13Cr5 IS 1570 (Part 4) 30Ni16Cr5
Tensile Strength 1550 MPa min >=1540 MPa
Yield Strength (0.2% proof) 1300 MPa min Not specified
Elongation >=8% >=8%
Izod Impact 14 J min >=14 J
Hardness (annealed) <=250 HB Not specified
Condition Hardened and tempered Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 150 (oil hardened) mm
Yield Strength Not specified >=1240 MPa (0.2 % proof stress)
Hardness Not specified >=444 HBS (guidance only)
Key Differences
Can IS 5517 30Ni13Cr5 Be Substituted With IS 1570 (Part 4) 30Ni16Cr5?
IS 5517 30Ni13Cr5 and IS 1570 (Part 4) 30Ni16Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 5517 30Ni13Cr5
0 active listings and RFQs →
IS 1570 (Part 4) 30Ni16Cr5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 30Ni13Cr5 and IS 1570 (Part 4) 30Ni16Cr5?
IS 5517 30Ni13Cr5 specifies S, P which are not specified for IS 1570 (Part 4) 30Ni16Cr5.
Can IS 5517 30Ni13Cr5 be substituted with IS 1570 (Part 4) 30Ni16Cr5?
IS 5517 30Ni13Cr5 and IS 1570 (Part 4) 30Ni16Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.