IS 5517 31Ni10Cr3Mo6 vs IS 4367 07Cr4Mo6

Minimal Match — 46.3% match based on chemical composition and mechanical property overlap.

IS 5517 31Ni10Cr3Mo6 (IS 5517:1993) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 5517 31Ni10Cr3Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 5517 31Ni10Cr3Mo6 vs IS 4367 07Cr4Mo6 is a 69.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 46.3%.

Frequently Compared With IS 5517 31Ni10Cr3Mo6:
UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
69.4%
MECHANICAL MATCH
0%
OVERALL
46.3%
Specifications
Property IS 5517 31Ni10Cr3Mo6 IS 4367 07Cr4Mo6
Standard IS 5517:1993 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.27-0.35 <=0.12
Si (%) 0.10-0.35 0.15-0.60
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 2.25-2.75 <=0.30
Cr (%) 0.50-0.80 0.70-1.10
Mo (%) 0.40-0.70 0.45-0.65
S (%) <=0.035 <=0.035
P (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 31Ni10Cr3Mo6 IS 4367 07Cr4Mo6
Tensile Strength 900-1050 MPa 380-550 MPa
Yield Strength (0.2% proof) 700 MPa min Not specified
Elongation >=15% >=19%
Izod Impact 55 J min 60 J min
Hardness (annealed) <=269 HB Not specified
Condition Hardened and tempered, ruling section up to 150 mm Normalised and tempered, ruling section up to 40 mm
Yield Strength Not specified 225 MPa min
Hardness (soft annealed) Not specified <=170 HB
Can IS 5517 31Ni10Cr3Mo6 Be Substituted With IS 4367 07Cr4Mo6?
IS 5517 31Ni10Cr3Mo6 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 5517 31Ni10Cr3Mo6
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 31Ni10Cr3Mo6 and IS 4367 07Cr4Mo6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5517 31Ni10Cr3Mo6 be substituted with IS 4367 07Cr4Mo6?
IS 5517 31Ni10Cr3Mo6 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.