IS 5517:1993 37C15 Steel: Specifications & Listings
IS 5517:1993 37C15: 37C15 is a steel in IS 5517:1993 (Steels for Hardening and Tempering), intended in general for forgings and machined parts for engineering or automobile purposes.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
S
P
0.32-0.42
0.10-0.35
1.30-1.70
<=0.035
<=0.035
Mechanical Properties
Tensile Strength
600-750 MPa
Yield Strength (0.2% proof)
440 MPa min
Elongation
>=18%
Izod Impact
48 J min
Hardness (annealed)
<=220 HB
Condition
Hardened and tempered, ruling section up to 100 mm
More data from IS 5517:1993
From the standard
Heat treatment temperatures5 values
Hot working temperature
1200 to 850 °C
Normalising temperature
850 to 870 °C
Hardening temperature
850 to 870 °C
Quenching medium
Water or Oil
Tempering temperature
550 to 660 °C
Source: IS 5517:1993 with Amendments 1 to 3, Table 4
Properties after hardening and tempering, by ruling section4 sections
Tensile strength (MPa)
0.2% proof stress, min (MPa)
Elongation, min (%)
Izod impact, min (J)
Limiting ruling section (mm)
600 to 750
440
18
48
100
700 to 850
540
18
48
63
800 to 950
600
16
48
30
900 to 1050
700
15
41
15
Values apply to test bars taken from rounds along the direction of rolling. Izod impact values are for fine grained steels.
Source: IS 5517:1993 with Amendments 1 to 3, Table 5
Hardness by delivery condition3 conditions
As annealed (A), maximum
220 HB
As rolled (R), maximum
250 HB
Treated for improved machinability (M), maximum
229 HB
For improved machinability the microstructure of the steel may be mutually agreed between the manufacturer and the purchaser.
Source: IS 5517:1993 with Amendments 1 to 3, Table 6