Strong Match — 94.2% match
based on chemical composition and mechanical property overlap.
IS 5517 40C8 (IS 5517:1993) and BS 970 (Part 3) 080M40 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Carbon Steel category.
IS 5517 40C8 is typically used for crankshafts, couplings, bolts, spindles, axles, gears, while BS 970 (Part 3) 080M40 is commonly used for shafts, gears, axles, general engineering.
IS 5517 40C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 080M40 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, IS 5517 40C8 vs BS 970 (Part 3) 080M40 is a 94.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 94.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Can IS 5517 40C8 Be Substituted With BS 970 (Part 3) 080M40?
IS 5517 40C8 and BS 970 (Part 3) 080M40 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080M40 is often considered as a substitute for IS 5517 40C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 5517 40C8 and BS 970 (Part 3) 080M40?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5517 40C8 be substituted with BS 970 (Part 3) 080M40?
IS 5517 40C8 and BS 970 (Part 3) 080M40 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 080M40 is often considered as a substitute for IS 5517 40C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.