IS 5517 40Ni10Cr3Mo6 vs IS 11169 (Part 1) 10Ni5Cr4

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 5517 40Ni10Cr3Mo6 (IS 5517:1993) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 5517 40Ni10Cr3Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 5517 40Ni10Cr3Mo6 vs IS 11169 (Part 1) 10Ni5Cr4 is a 54.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 5517 40Ni10Cr3Mo6:
IS 1570 (Part 7) 10Cr36Mo10H NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
54.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 5517 40Ni10Cr3Mo6 IS 11169 (Part 1) 10Ni5Cr4
Standard IS 5517:1993 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.36-0.44 0.07-0.12
Si (%) 0.10-0.35 <=0.30
Mn (%) 0.40-0.70 0.60-0.90
Ni (%) 2.25-2.75 1.20-1.50
Cr (%) 0.50-0.80 0.90-1.20
Mo (%) 0.40-0.70 Not specified
S (%) <=0.035 <=0.025
P (%) <=0.035 <=0.025
Cu (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 5517 40Ni10Cr3Mo6 IS 11169 (Part 1) 10Ni5Cr4
Tensile Strength 1000-1150 MPa Not specified
Yield Strength (0.2% proof) 800 MPa min Not specified
Elongation >=12% Not specified
Izod Impact 48 J min Not specified
Hardness (annealed) <=269 HB Not specified
Condition Hardened and tempered, ruling section up to 150 mm Not specified
Hardness, ferrite-pearlite (+FP) Not specified 137-187 HB
Tensile Strength, annealed (+AC) Not specified <=520 MPa (over 5 to 40 mm)
Typical Applications
IS 5517 40Ni10Cr3Mo6
Not documented
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 5517 40Ni10Cr3Mo6 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
IS 5517 40Ni10Cr3Mo6 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 5517 40Ni10Cr3Mo6
0 active listings and RFQs →
IS 11169 (Part 1) 10Ni5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 5517 40Ni10Cr3Mo6 and IS 11169 (Part 1) 10Ni5Cr4?
IS 5517 40Ni10Cr3Mo6 specifies Mo which is not specified for IS 11169 (Part 1) 10Ni5Cr4. IS 11169 (Part 1) 10Ni5Cr4 specifies Cu which is not specified for IS 5517 40Ni10Cr3Mo6.
Can IS 5517 40Ni10Cr3Mo6 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
IS 5517 40Ni10Cr3Mo6 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.