Minimal Match — 25.8% match
based on chemical composition and mechanical property overlap.
IS 6603 X01Cr24Ni22Mo4CuNW (IS 6603:2024) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X01Cr24Ni22Mo4CuNW is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments.
IS 6603 X01Cr24Ni22Mo4CuNW is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6603 X01Cr24Ni22Mo4CuNW vs EN 10088-1 1.4006 is a 38.7% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 25.8%.
Frequently Compared With IS 6603 X01Cr24Ni22Mo4CuNW:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X01Cr24Ni22Mo4CuNW
EN 10088-1 1.4006
Tensile Strength
800-1000 MPa
≥540 MPa (annealed)
Yield Strength
>=420 MPa
Not specified
Elongation
>=50%
≥18%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 60 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Not specified
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
IS 6603 X01Cr24Ni22Mo4CuNW
General purposes, semi-finished products, bars, wire rods and bright bars
IS 6603 X01Cr24Ni22Mo4CuNW specifies P, S, Mo, N which are not specified for EN 10088-1 1.4006.
Can IS 6603 X01Cr24Ni22Mo4CuNW Be Substituted With EN 10088-1 1.4006?
IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 1.4006?
IS 6603 X01Cr24Ni22Mo4CuNW specifies P, S, Mo, N which are not specified for EN 10088-1 1.4006.
Can IS 6603 X01Cr24Ni22Mo4CuNW be substituted with EN 10088-1 1.4006?
IS 6603 X01Cr24Ni22Mo4CuNW and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.