Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 6603 X01Cr24Ni22Mo7CuN (IS 6603:2024) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X01Cr24Ni22Mo7CuN is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 6603 X01Cr24Ni22Mo7CuN is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 6603 X01Cr24Ni22Mo7CuN vs GOST 5632 08X18H10 is a 47.5% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 6603 X01Cr24Ni22Mo7CuN:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X01Cr24Ni22Mo7CuN
GOST 5632 08X18H10
Tensile Strength
750-1050 MPa
≥520 MPa
Yield Strength
>=430 MPa
≥205 MPa
Elongation
>=40%
≥40%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Not specified
Typical Applications
IS 6603 X01Cr24Ni22Mo7CuN
General purposes, semi-finished products, bars, wire rods and bright bars
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
IS 6603 X01Cr24Ni22Mo7CuN specifies Mo, N, Cu which are not specified for GOST 5632 08X18H10.
Can IS 6603 X01Cr24Ni22Mo7CuN Be Substituted With GOST 5632 08X18H10?
IS 6603 X01Cr24Ni22Mo7CuN and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6603 X01Cr24Ni22Mo7CuN and GOST 5632 08X18H10?
IS 6603 X01Cr24Ni22Mo7CuN specifies Mo, N, Cu which are not specified for GOST 5632 08X18H10.
Can IS 6603 X01Cr24Ni22Mo7CuN be substituted with GOST 5632 08X18H10?
IS 6603 X01Cr24Ni22Mo7CuN and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.