Minimal Match — 32.2% match
based on chemical composition and mechanical property overlap.
IS 6603 X01Ni25Cr20Mo7CuN (IS 6603:2024) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X01Ni25Cr20Mo7CuN is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
IS 6603 X01Ni25Cr20Mo7CuN is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 6603 X01Ni25Cr20Mo7CuN vs GOST 5632 06Kh23N28 is a 48.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 32.2%.
Frequently Compared With IS 6603 X01Ni25Cr20Mo7CuN:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X01Ni25Cr20Mo7CuN
GOST 5632 06Kh23N28
Tensile Strength
650-850 MPa
≥510 MPa
Yield Strength
>=300 MPa
≥196 MPa
Elongation
>=40%
≥35%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Not specified
Max Service Temp
Not specified
1050°C
Typical Applications
IS 6603 X01Ni25Cr20Mo7CuN
General purposes, semi-finished products, bars, wire rods and bright bars
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
IS 6603 X01Ni25Cr20Mo7CuN specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can IS 6603 X01Ni25Cr20Mo7CuN Be Substituted With GOST 5632 06Kh23N28?
IS 6603 X01Ni25Cr20Mo7CuN and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6603 X01Ni25Cr20Mo7CuN and GOST 5632 06Kh23N28?
IS 6603 X01Ni25Cr20Mo7CuN specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can IS 6603 X01Ni25Cr20Mo7CuN be substituted with GOST 5632 06Kh23N28?
IS 6603 X01Ni25Cr20Mo7CuN and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.