Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Mo
Ni
N
Cu
<=0.020
<=0.70
<=2.00
<=0.030
<=0.010
26.0-28.0
3.0-4.0
30.0-32.0
<=0.10
0.70-1.50
Mechanical Properties
Tensile Strength
500-750 MPa
Yield Strength
>=220 MPa
Elongation
>=35%
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
More data from IS 6603:2024
From the standard
Mechanical properties by thickness or diameter2 size ranges
Thickness or diameter (mm)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 160
220
259
500 to 750
35
-
100
-
over 160 to 250
220
259
500 to 750
-
30
-
60
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; elongation and proof strength are not valid for rod.
Source: IS 6603:2024, Table 5
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
190
220
150
175
205
200
160
190
250
155
185
300
150
180
350
145
175
400
135
165
450
125
155
500
120
150
550
115
145
Minimum values, solution annealed (+AT); for guidance only.
Source: IS 6603:2024, Table 10
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1050 to 1150 deg C
Cooling after solution annealing
water, air (rapid cooling)
Informative guideline (Annex A).
Source: IS 6603:2024, Table 20