IS 6603 X02Cr18Mo2TiS vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr18Mo2TiS (IS 6603:2024) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr18Mo2TiS is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 6603 X02Cr18Mo2TiS is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr18Mo2TiS vs EN 10088-1 1.4006 is a 55.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6603 X02Cr18Mo2TiS:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
55.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6603 X02Cr18Mo2TiS EN 10088-1 1.4006
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=0.50 ≤1.50
P (%) <=0.040 Not specified
S (%) >=0.15 Not specified
Cr (%) 17.5-19.0 11.5–13.5
Mo (%) 2.00-2.50 Not specified
Ti (%) 0.30-0.80 Not specified
Ni (%) Not specified ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr18Mo2TiS EN 10088-1 1.4006
Tensile Strength >=430 MPa ≥540 MPa (annealed)
Yield Strength >=280 MPa Not specified
Elongation >=15% ≥18%
Hardness <=200 HB Not specified
Condition Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Tensile Strength is a minimum as printed Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 6603 X02Cr18Mo2TiS
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 6603 X02Cr18Mo2TiS Be Substituted With EN 10088-1 1.4006?
IS 6603 X02Cr18Mo2TiS and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6603 X02Cr18Mo2TiS
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 6603 X02Cr18Mo2TiS
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr18Mo2TiS and EN 10088-1 1.4006?
IS 6603 X02Cr18Mo2TiS specifies P, S, Mo, Ti which are not specified for EN 10088-1 1.4006. EN 10088-1 1.4006 specifies Ni which is not specified for IS 6603 X02Cr18Mo2TiS.
Can IS 6603 X02Cr18Mo2TiS be substituted with EN 10088-1 1.4006?
IS 6603 X02Cr18Mo2TiS and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.