IS 6603 X02Cr18Ni12Mo3N vs ASTM A959 317L

Strong Match — 86.9% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr18Ni12Mo3N (IS 6603:2024) and ASTM A959 317L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr18Ni12Mo3N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 317L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 6603 X02Cr18Ni12Mo3N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 317L is defined under ASTM International, originating from United States.

As per chemical composition, IS 6603 X02Cr18Ni12Mo3N vs ASTM A959 317L is a 86.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.9%.

Frequently Compared With IS 6603 X02Cr18Ni12Mo3N:
GOST 5632 08X18H10 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
86.9%
MECHANICAL MATCH
No shared data
OVERALL
86.9%
Specifications
Property IS 6603 X02Cr18Ni12Mo3N ASTM A959 317L
Standard IS 6603:2024 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.5-19.5 18.0-20.0
Mo (%) 3.0-4.0 3.0-4.0
Ni (%) 10.5-14.0 11.0-15.0
N (%) 0.10-0.20 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr18Ni12Mo3N ASTM A959 317L
Tensile Strength 540-740 MPa Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, rod only; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X02Cr18Ni12Mo3N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 317L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 6603 X02Cr18Ni12Mo3N Be Substituted With ASTM A959 317L?
IS 6603 X02Cr18Ni12Mo3N and ASTM A959 317L overlap closely enough on chemistry and mechanical properties that ASTM A959 317L is often considered as a substitute for IS 6603 X02Cr18Ni12Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X02Cr18Ni12Mo3N
0 active listings and RFQs →
ASTM A959 317L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr18Ni12Mo3N and ASTM A959 317L?
IS 6603 X02Cr18Ni12Mo3N specifies N which is not specified for ASTM A959 317L.
Can IS 6603 X02Cr18Ni12Mo3N be substituted with ASTM A959 317L?
IS 6603 X02Cr18Ni12Mo3N and ASTM A959 317L overlap closely enough on chemistry and mechanical properties that ASTM A959 317L is often considered as a substitute for IS 6603 X02Cr18Ni12Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.