IS 6603 X02Cr18TiNb vs EN 10088-1 X2CrTiNb18

Strong Match — 94.7% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr18TiNb (IS 6603:2024) and EN 10088-1 X2CrTiNb18 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr18TiNb is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrTiNb18 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr18TiNb vs EN 10088-1 X2CrTiNb18 is a 94.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.7%.

Frequently Compared With IS 6603 X02Cr18TiNb:
ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
94.7%
MECHANICAL MATCH
No shared data
OVERALL
94.7%
Specifications
Property IS 6603 X02Cr18TiNb EN 10088-1 X2CrTiNb18
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.015
Cr (%) 17.5-18.5 17.5-18.5
Ti (%) 0.10-0.60 0.10-0.60
Nb (%) <=1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr18TiNb EN 10088-1 X2CrTiNb18
Tensile Strength >=420 MPa Not specified
Yield Strength >=200 MPa Not specified
Elongation >=28% Not specified
Hardness <=200 HB Not specified
Condition Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; Tensile Strength is a minimum as printed Not specified
Typical Applications
IS 6603 X02Cr18TiNb
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X2CrTiNb18
Not documented
Key Differences
Can IS 6603 X02Cr18TiNb Be Substituted With EN 10088-1 X2CrTiNb18?
IS 6603 X02Cr18TiNb and EN 10088-1 X2CrTiNb18 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrTiNb18 is often considered as a substitute for IS 6603 X02Cr18TiNb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X02Cr18TiNb
0 active listings and RFQs →
EN 10088-1 X2CrTiNb18
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr18TiNb and EN 10088-1 X2CrTiNb18?
IS 6603 X02Cr18TiNb specifies Nb which is not specified for EN 10088-1 X2CrTiNb18.
Can IS 6603 X02Cr18TiNb be substituted with EN 10088-1 X2CrTiNb18?
IS 6603 X02Cr18TiNb and EN 10088-1 X2CrTiNb18 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrTiNb18 is often considered as a substitute for IS 6603 X02Cr18TiNb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.