IS 6603 X02Cr19Ni10 (IS 6603:2024) and BS 970 (Part 1) 304S11 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr19Ni10 is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while BS 970 (Part 1) 304S11 is commonly used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition).. IS 6603 X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 304S11 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 6603 X02Cr19Ni10 vs BS 970 (Part 1) 304S11 is a 92.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.4%.

Frequently Compared With IS 6603 X02Cr19Ni10:
EN 10088-1 1.4301 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
92.4%
MECHANICAL MATCH
No shared data
OVERALL
92.4%
Specifications
Property IS 6603 X02Cr19Ni10 BS 970 (Part 1) 304S11
Standard IS 6603:2024 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 17.0-20.0 17.0-19.0
Ni (%) 8.0-12.0 9.0-12.0
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr19Ni10 BS 970 (Part 1) 304S11
Tensile Strength 480-680 MPa Not specified
Yield Strength >=180 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X02Cr19Ni10
General purposes, semi-finished products, bars, wire rods and bright bars
BS 970 (Part 1) 304S11
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Key Differences
Can IS 6603 X02Cr19Ni10 Be Substituted With BS 970 (Part 1) 304S11?
IS 6603 X02Cr19Ni10 and BS 970 (Part 1) 304S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 304S11 is often considered as a substitute for IS 6603 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X02Cr19Ni10
0 active listings and RFQs →
BS 970 (Part 1) 304S11
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr19Ni10 and BS 970 (Part 1) 304S11?
IS 6603 X02Cr19Ni10 specifies N which is not specified for BS 970 (Part 1) 304S11.
Can IS 6603 X02Cr19Ni10 be substituted with BS 970 (Part 1) 304S11?
IS 6603 X02Cr19Ni10 and BS 970 (Part 1) 304S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 304S11 is often considered as a substitute for IS 6603 X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.