Strong Match — 90.1% match
based on chemical composition and mechanical property overlap.
IS 6603 X02Cr22Ni2N (IS 6603:2024) and ASTM A276/A276M S32202 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X02Cr22Ni2N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A276/A276M S32202 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
IS 6603 X02Cr22Ni2N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S32202 is defined under ASTM International, originating from United States.
As per chemical composition, IS 6603 X02Cr22Ni2N vs ASTM A276/A276M S32202 is a 97.7% match.
As per mechanical properties, the match is 75%.
Combined, this makes them a strong match overall at 90.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X02Cr22Ni2N
ASTM A276/A276M S32202
Tensile Strength
>=650 MPa
>=650 MPa
Yield Strength
>=380 MPa
>=450 MPa
Elongation
>=30%
>=30%
Hardness
<=290 HB
<=290 HB
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
IS 6603 X02Cr22Ni2N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A276/A276M S32202
Stainless steel bars and shapes (hot-finished or cold-finished)
Can IS 6603 X02Cr22Ni2N Be Substituted With ASTM A276/A276M S32202?
IS 6603 X02Cr22Ni2N and ASTM A276/A276M S32202 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32202 is often considered as a substitute for IS 6603 X02Cr22Ni2N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6603 X02Cr22Ni2N and ASTM A276/A276M S32202?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X02Cr22Ni2N be substituted with ASTM A276/A276M S32202?
IS 6603 X02Cr22Ni2N and ASTM A276/A276M S32202 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S32202 is often considered as a substitute for IS 6603 X02Cr22Ni2N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.