IS 6603 X02Cr25Ni18Mn6Mo4N vs EN 10088-1 X2CrNiMoN25-7-4

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr25Ni18Mn6Mo4N (IS 6603:2024) and EN 10088-1 X2CrNiMoN25-7-4 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr25Ni18Mn6Mo4N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr25Ni18Mn6Mo4N vs EN 10088-1 X2CrNiMoN25-7-4 is a 70.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 6603 X02Cr25Ni18Mn6Mo4N:
EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
70.1%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 6603 X02Cr25Ni18Mn6Mo4N EN 10088-1 X2CrNiMoN25-7-4
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-7.0 <=2.00
P (%) <=0.030 <=0.035
S (%) <=0.010 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 4.0-5.0 3.00-4.5
Ni (%) 16.0-19.0 6.0-8.0
N (%) 0.30-0.60 0.24-0.35
Nb (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr25Ni18Mn6Mo4N EN 10088-1 X2CrNiMoN25-7-4
Tensile Strength 800-1000 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=35% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X02Cr25Ni18Mn6Mo4N
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X2CrNiMoN25-7-4
Not documented
Key Differences
Can IS 6603 X02Cr25Ni18Mn6Mo4N Be Substituted With EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-1 X2CrNiMoN25-7-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X02Cr25Ni18Mn6Mo4N
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni18Mn6Mo4N specifies Nb which is not specified for EN 10088-1 X2CrNiMoN25-7-4.
Can IS 6603 X02Cr25Ni18Mn6Mo4N be substituted with EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni18Mn6Mo4N and EN 10088-1 X2CrNiMoN25-7-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.