IS 6603 X02Cr25Ni6Mo3CuN vs EN 10088-1 X2CrNiMoN25-7-4

Close Alternative — 83.3% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr25Ni6Mo3CuN (IS 6603:2024) and EN 10088-1 X2CrNiMoN25-7-4 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr25Ni6Mo3CuN is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr25Ni6Mo3CuN vs EN 10088-1 X2CrNiMoN25-7-4 is a 83.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.3%.

Frequently Compared With IS 6603 X02Cr25Ni6Mo3CuN:
EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 255 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
83.3%
MECHANICAL MATCH
No shared data
OVERALL
83.3%
Specifications
Property IS 6603 X02Cr25Ni6Mo3CuN EN 10088-1 X2CrNiMoN25-7-4
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.70 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 2.5-4.0 3.00-4.5
Ni (%) 5.0-7.5 6.0-8.0
N (%) 0.15-0.30 0.24-0.35
Cu (%) 1.00-2.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr25Ni6Mo3CuN EN 10088-1 X2CrNiMoN25-7-4
Tensile Strength >=700 MPa Not specified
Yield Strength >=500 MPa Not specified
Elongation >=25% Not specified
Hardness <=270 HB Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only Not specified
Typical Applications
IS 6603 X02Cr25Ni6Mo3CuN
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X2CrNiMoN25-7-4
Not documented
Key Differences
Can IS 6603 X02Cr25Ni6Mo3CuN Be Substituted With EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni6Mo3CuN and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 6603 X02Cr25Ni6Mo3CuN
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr25Ni6Mo3CuN and EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni6Mo3CuN specifies Cu which is not specified for EN 10088-1 X2CrNiMoN25-7-4.
Can IS 6603 X02Cr25Ni6Mo3CuN be substituted with EN 10088-1 X2CrNiMoN25-7-4?
IS 6603 X02Cr25Ni6Mo3CuN and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.