Minimal Match — 29.6% match
based on chemical composition and mechanical property overlap.
IS 6603 X02Cr25Ni7Mo4CuWN (IS 6603:2024) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X02Cr25Ni7Mo4CuWN is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 6603 X02Cr25Ni7Mo4CuWN is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 6603 X02Cr25Ni7Mo4CuWN vs GOST 5632 08X18H10 is a 44.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 29.6%.
Frequently Compared With IS 6603 X02Cr25Ni7Mo4CuWN:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X02Cr25Ni7Mo4CuWN
GOST 5632 08X18H10
Tensile Strength
>=730 MPa
≥520 MPa
Yield Strength
>=530 MPa
≥205 MPa
Elongation
>=25%
≥40%
Hardness
<=290 HB
Not specified
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Not specified
Typical Applications
IS 6603 X02Cr25Ni7Mo4CuWN
General purposes, semi-finished products, bars, wire rods and bright bars
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
IS 6603 X02Cr25Ni7Mo4CuWN specifies Mo, N, Cu, W which are not specified for GOST 5632 08X18H10.
Can IS 6603 X02Cr25Ni7Mo4CuWN Be Substituted With GOST 5632 08X18H10?
IS 6603 X02Cr25Ni7Mo4CuWN and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6603 X02Cr25Ni7Mo4CuWN and GOST 5632 08X18H10?
IS 6603 X02Cr25Ni7Mo4CuWN specifies Mo, N, Cu, W which are not specified for GOST 5632 08X18H10.
Can IS 6603 X02Cr25Ni7Mo4CuWN be substituted with GOST 5632 08X18H10?
IS 6603 X02Cr25Ni7Mo4CuWN and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.