IS 6603 X02Cr28Ni8Mo5CoN vs EN 10088-1 X2CrNiMoN29-7-2

Related Material — 67.5% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr28Ni8Mo5CoN (IS 6603:2024) and EN 10088-1 X2CrNiMoN29-7-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr28Ni8Mo5CoN is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoN29-7-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X02Cr28Ni8Mo5CoN vs EN 10088-1 X2CrNiMoN29-7-2 is a 67.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.5%.

Frequently Compared With IS 6603 X02Cr28Ni8Mo5CoN:
EN 10088-1 1.4006 EN 10088-1 1.4845 GOST 5632 08X18H10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
67.5%
MECHANICAL MATCH
No shared data
OVERALL
67.5%
Specifications
Property IS 6603 X02Cr28Ni8Mo5CoN EN 10088-1 X2CrNiMoN29-7-2
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.50 <=0.50
Mn (%) <=1.50 0.80-1.50
P (%) <=0.035 <=0.030
S (%) <=0.010 <=0.015
Cr (%) 26.0-29.0 28.0-30.0
Mo (%) 4.0-5.0 1.50-2.60
Ni (%) 5.5-9.5 5.8-7.5
N (%) 0.30-0.50 0.30-0.40
Cu (%) <=1.00 <=0.80
Co (%) 0.50-2.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr28Ni8Mo5CoN EN 10088-1 X2CrNiMoN29-7-2
Tensile Strength >=800 MPa Not specified
Yield Strength >=650 MPa Not specified
Elongation >=25% Not specified
Hardness <=300 HB Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 5 mm; Tensile Strength is a minimum as printed, hardness for guidance only Not specified
Typical Applications
IS 6603 X02Cr28Ni8Mo5CoN
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X2CrNiMoN29-7-2
Not documented
Key Differences
Can IS 6603 X02Cr28Ni8Mo5CoN Be Substituted With EN 10088-1 X2CrNiMoN29-7-2?
IS 6603 X02Cr28Ni8Mo5CoN and EN 10088-1 X2CrNiMoN29-7-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X02Cr28Ni8Mo5CoN
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN29-7-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr28Ni8Mo5CoN and EN 10088-1 X2CrNiMoN29-7-2?
IS 6603 X02Cr28Ni8Mo5CoN specifies Co which is not specified for EN 10088-1 X2CrNiMoN29-7-2.
Can IS 6603 X02Cr28Ni8Mo5CoN be substituted with EN 10088-1 X2CrNiMoN29-7-2?
IS 6603 X02Cr28Ni8Mo5CoN and EN 10088-1 X2CrNiMoN29-7-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.