IS 6603 X03Cr17Nb vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6603 X03Cr17Nb (IS 6603:2024) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X03Cr17Nb is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. IS 6603 X03Cr17Nb is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X03Cr17Nb vs EN 10088-1 1.4301 is a 66.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6603 X03Cr17Nb:
EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
66.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6603 X03Cr17Nb EN 10088-1 1.4301
Standard IS 6603:2024 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.05 ≤0.07
Si (%) <=1.00 ≤1.00
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 ≤0.045
S (%) <=0.015 ≤0.030
Cr (%) 16.0-18.0 17.5–19.5
Nb (%) <=1.00 Not specified
Ni (%) Not specified 8.0–10.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X03Cr17Nb EN 10088-1 1.4301
Tensile Strength >=420 MPa ≥520 MPa
Yield Strength >=230 MPa ≥210 MPa
Elongation >=20% ≥45%
Condition Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Tensile Strength is a minimum as printed Not specified
Hardness Not specified ≤215 HB
Typical Applications
IS 6603 X03Cr17Nb
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can IS 6603 X03Cr17Nb Be Substituted With EN 10088-1 1.4301?
IS 6603 X03Cr17Nb and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6603 X03Cr17Nb
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
IS 6603 X03Cr17Nb
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X03Cr17Nb and EN 10088-1 1.4301?
IS 6603 X03Cr17Nb specifies Nb which is not specified for EN 10088-1 1.4301. EN 10088-1 1.4301 specifies Ni which is not specified for IS 6603 X03Cr17Nb.
Can IS 6603 X03Cr17Nb be substituted with EN 10088-1 1.4301?
IS 6603 X03Cr17Nb and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.