IS 6603 X06Cr18Ni9Cu2S vs EN 10088-1 X10CrNi18-8

Close Alternative — 76% match based on chemical composition and mechanical property overlap.

IS 6603 X06Cr18Ni9Cu2S (IS 6603:2024) and EN 10088-1 X10CrNi18-8 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X06Cr18Ni9Cu2S is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X10CrNi18-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X06Cr18Ni9Cu2S vs EN 10088-1 X10CrNi18-8 is a 76% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76%.

Frequently Compared With IS 6603 X06Cr18Ni9Cu2S:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
76%
MECHANICAL MATCH
No shared data
OVERALL
76%
Specifications
Property IS 6603 X06Cr18Ni9Cu2S EN 10088-1 X10CrNi18-8
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.030-0.15
Si (%) <=1.00 <=2.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) >=0.15 <=0.015
Cr (%) 17.0-19.0 16.0-19.0
Mo (%) <=0.60 <=0.80
Ni (%) 8.0-10.0 6.0-9.5
N (%) <=0.10 <=0.10
Cu (%) 1.40-1.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X06Cr18Ni9Cu2S EN 10088-1 X10CrNi18-8
Tensile Strength 500-710 MPa Not specified
Yield Strength >=185 MPa Not specified
Elongation >=35% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X06Cr18Ni9Cu2S
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X10CrNi18-8
Not documented
Key Differences
Can IS 6603 X06Cr18Ni9Cu2S Be Substituted With EN 10088-1 X10CrNi18-8?
IS 6603 X06Cr18Ni9Cu2S and EN 10088-1 X10CrNi18-8 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 6603 X06Cr18Ni9Cu2S
0 active listings and RFQs →
EN 10088-1 X10CrNi18-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X06Cr18Ni9Cu2S and EN 10088-1 X10CrNi18-8?
IS 6603 X06Cr18Ni9Cu2S specifies Cu which is not specified for EN 10088-1 X10CrNi18-8.
Can IS 6603 X06Cr18Ni9Cu2S be substituted with EN 10088-1 X10CrNi18-8?
IS 6603 X06Cr18Ni9Cu2S and EN 10088-1 X10CrNi18-8 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.