Strong Match — 100% match
based on chemical composition and mechanical property overlap.
IS 6603 X07Cr17Ni7Al (IS 6603:2024) and EN 10088-3 X7CrNiAl17-7 (EN 10088-3:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X07Cr17Ni7Al is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while EN 10088-3 X7CrNiAl17-7 is commonly used for general purposes, semi-finished products, bars, rods, wire, sections and bright products.
IS 6603 X07Cr17Ni7Al is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-3 X7CrNiAl17-7 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6603 X07Cr17Ni7Al vs EN 10088-3 X7CrNiAl17-7 is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X07Cr17Ni7Al
EN 10088-3 X7CrNiAl17-7
Tensile Strength
<=850 MPa
<=850 MPa
Hardness
<=255 HB
<=255 HB
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D; hardness as printed
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 30 mm; hardness for guidance only
Typical Applications
IS 6603 X07Cr17Ni7Al
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-3 X7CrNiAl17-7
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can IS 6603 X07Cr17Ni7Al Be Substituted With EN 10088-3 X7CrNiAl17-7?
IS 6603 X07Cr17Ni7Al and EN 10088-3 X7CrNiAl17-7 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X7CrNiAl17-7 is often considered as a substitute for IS 6603 X07Cr17Ni7Al in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6603 X07Cr17Ni7Al and EN 10088-3 X7CrNiAl17-7?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X07Cr17Ni7Al be substituted with EN 10088-3 X7CrNiAl17-7?
IS 6603 X07Cr17Ni7Al and EN 10088-3 X7CrNiAl17-7 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X7CrNiAl17-7 is often considered as a substitute for IS 6603 X07Cr17Ni7Al in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.