Strong Match — 94.2% match
based on chemical composition and mechanical property overlap.
IS 6603 X12Cr18Mn9Ni5N (IS 6603:2024) and ASTM A959 202 (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
IS 6603 X12Cr18Mn9Ni5N is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 202 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1).
IS 6603 X12Cr18Mn9Ni5N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 202 is defined under ASTM International, originating from United States.
As per chemical composition, IS 6603 X12Cr18Mn9Ni5N vs ASTM A959 202 is a 94.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 94.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6603 X12Cr18Mn9Ni5N
ASTM A959 202
Tensile Strength
700-900 MPa
Not specified
Yield Strength
>=350 MPa
Not specified
Elongation
>=35%
Not specified
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 10 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Not specified
Typical Applications
IS 6603 X12Cr18Mn9Ni5N
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 202
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 6603 X12Cr18Mn9Ni5N Be Substituted With ASTM A959 202?
IS 6603 X12Cr18Mn9Ni5N and ASTM A959 202 overlap closely enough on chemistry and mechanical properties that ASTM A959 202 is often considered as a substitute for IS 6603 X12Cr18Mn9Ni5N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6603 X12Cr18Mn9Ni5N and ASTM A959 202?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X12Cr18Mn9Ni5N be substituted with ASTM A959 202?
IS 6603 X12Cr18Mn9Ni5N and ASTM A959 202 overlap closely enough on chemistry and mechanical properties that ASTM A959 202 is often considered as a substitute for IS 6603 X12Cr18Mn9Ni5N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.