Post Stock Login Register

IS 6603 X14Cr17S vs EN 10088-1 X6CrMoS17

Close Alternative — 84.3% match based on chemical composition and mechanical property overlap.

IS 6603 X14Cr17S (IS 6603:2024) and EN 10088-1 X6CrMoS17 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X14Cr17S is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6CrMoS17 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X14Cr17S vs EN 10088-1 X6CrMoS17 is a 84.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.3%.

Frequently Compared With IS 6603 X14Cr17S:
ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
84.3%
MECHANICAL MATCH
No shared data
OVERALL
84.3%
Specifications
Property IS 6603 X14Cr17S EN 10088-1 X6CrMoS17
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.10-0.17 <=0.08
Si (%) <=1.00 <=1.50
Mn (%) <=1.50 <=1.50
P (%) <=0.040 <=0.040
S (%) >=0.15 0.15-0.35
Cr (%) 16.0-18.0 16.0-18.0
Mo (%) <=0.60 0.20-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X14Cr17S EN 10088-1 X6CrMoS17
Tensile Strength <=730 MPa Not specified
Hardness <=220 HB Not specified
Condition Soft annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, all sizes; hardness as printed Not specified
Typical Applications
IS 6603 X14Cr17S
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X6CrMoS17
Not documented
Can IS 6603 X14Cr17S Be Substituted With EN 10088-1 X6CrMoS17?
IS 6603 X14Cr17S and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 6603 X14Cr17S
0 active listings and RFQs →
EN 10088-1 X6CrMoS17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X14Cr17S and EN 10088-1 X6CrMoS17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6603 X14Cr17S be substituted with EN 10088-1 X6CrMoS17?
IS 6603 X14Cr17S and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.