Related Material — 56.4% match
based on chemical composition and mechanical property overlap.
IS 6911 X02Cr19Ni10 (IS 6911:1992) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6911 X02Cr19Ni10 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
IS 6911 X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6911 X02Cr19Ni10 vs EN 10088-1 1.4845 is a 67.9% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a related material overall at 56.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6911 X02Cr19Ni10
EN 10088-1 1.4845
Bend Test (180 deg)
Not required
Not specified
Elongation (50 mm, annealed)
>=40%
Not specified
Hardness (annealed, max)
192 HBS, 88 HRB
Not specified
Tensile Strength (annealed)
>=440 MPa
Not specified
Yield Strength (0.2% proof, annealed)
>=180 MPa
Not specified
Tensile Strength
Not specified
≥515 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Max Service Temp
Not specified
1100°C continuous
Typical Applications
IS 6911 X02Cr19Ni10
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
IS 6911 X02Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 6911 X02Cr19Ni10 Be Substituted With EN 10088-1 1.4845?
IS 6911 X02Cr19Ni10 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 6911 X02Cr19Ni10 and EN 10088-1 1.4845?
IS 6911 X02Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 6911 X02Cr19Ni10 be substituted with EN 10088-1 1.4845?
IS 6911 X02Cr19Ni10 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.