IS 6911 X04Cr17Ni12Mo2Ti vs IS 1570 (Part 7) 12Cr12MoH

Minimal Match — 39.9% match based on chemical composition and mechanical property overlap.

IS 6911 X04Cr17Ni12Mo2Ti (IS 6911:1992) and IS 1570 (Part 7) 12Cr12MoH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X04Cr17Ni12Mo2Ti is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while IS 1570 (Part 7) 12Cr12MoH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 6911 X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr12MoH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 6911 X04Cr17Ni12Mo2Ti vs IS 1570 (Part 7) 12Cr12MoH is a 59.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 39.9%.

Frequently Compared With IS 6911 X04Cr17Ni12Mo2Ti:
EN 10088-1 1.4006 EN 10088-1 1.4845 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 12Kh13
Match Breakdown
CHEMISTRY MATCH
59.9%
MECHANICAL MATCH
0%
OVERALL
39.9%
Specifications
Property IS 6911 X04Cr17Ni12Mo2Ti IS 1570 (Part 7) 12Cr12MoH
Standard IS 6911:1992 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08-0.16
Cr (%) 16.0-18.0 11.5-13.00
Mn (%) <=2.0 0.40-1.00
Mo (%) 2.0-3.0 0.40-0.80
Ni (%) 10.0-14.0 <=1.0
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.035
Si (%) <=1.0 <=0.60
Ti (%) >=5x(C+N), <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X04Cr17Ni12Mo2Ti IS 1570 (Part 7) 12Cr12MoH
Bend Test (180 deg) Not required Not specified
Elongation (50 mm, annealed) >=35% Not specified
Hardness (annealed, max) 192 HBS, 95 HRB Not specified
Tensile Strength (annealed) >=490 MPa Not specified
Yield Strength (0.2% proof, annealed) >=220 MPa Not specified
Tensile Strength Not specified 680-880 MPa
Yield Strength Not specified >=490 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Condition Not specified Bars, forgings, Q+T, thickness up to 75 (first row of Table 3)
Typical Applications
IS 6911 X04Cr17Ni12Mo2Ti
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
IS 1570 (Part 7) 12Cr12MoH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 6911 X04Cr17Ni12Mo2Ti Be Substituted With IS 1570 (Part 7) 12Cr12MoH?
IS 6911 X04Cr17Ni12Mo2Ti and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6911 X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X04Cr17Ni12Mo2Ti and IS 1570 (Part 7) 12Cr12MoH?
IS 6911 X04Cr17Ni12Mo2Ti specifies Ti which is not specified for IS 1570 (Part 7) 12Cr12MoH.
Can IS 6911 X04Cr17Ni12Mo2Ti be substituted with IS 1570 (Part 7) 12Cr12MoH?
IS 6911 X04Cr17Ni12Mo2Ti and IS 1570 (Part 7) 12Cr12MoH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.