IS 6911 X108Cr17Mo vs ASTM A959 S42010

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 6911 X108Cr17Mo (IS 6911:1992) and ASTM A959 S42010 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X108Cr17Mo is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while ASTM A959 S42010 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 6911 X108Cr17Mo is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S42010 is defined under ASTM International, originating from United States.

As per chemical composition, IS 6911 X108Cr17Mo vs ASTM A959 S42010 is a 71.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 6911 X108Cr17Mo:
IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
71.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 6911 X108Cr17Mo ASTM A959 S42010
Standard IS 6911:1992 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 0.15-0.30
Cr (%) 16.0-18.0 13.5-15.0
Mn (%) <=1.0 <=1.00
Mo (%) <=0.75 0.40-0.85
Ni (%) <=0.50 0.35-0.85
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X108Cr17Mo ASTM A959 S42010
Hardness (annealed, max) 285 HBS Not specified
Hardness (quenched and tempered, min) 660 HV, 58 HRC Not specified
Typical Applications
IS 6911 X108Cr17Mo
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
ASTM A959 S42010
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 6911 X108Cr17Mo Be Substituted With ASTM A959 S42010?
IS 6911 X108Cr17Mo and ASTM A959 S42010 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6911 X108Cr17Mo
0 active listings and RFQs →
ASTM A959 S42010
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X108Cr17Mo and ASTM A959 S42010?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 6911 X108Cr17Mo be substituted with ASTM A959 S42010?
IS 6911 X108Cr17Mo and ASTM A959 S42010 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.