Strong Match — 92.8% match
based on chemical composition and mechanical property overlap.
IS 6911 X10Cr17Ni7 (IS 6911:1992) and EN 10088-1 X5CrNi17-7 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 6911 X10Cr17Ni7 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X5CrNi17-7 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 6911 X10Cr17Ni7 vs EN 10088-1 X5CrNi17-7 is a 92.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 92.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 6911 X10Cr17Ni7
EN 10088-1 X5CrNi17-7
Bend Test (180 deg)
Not required
Not specified
Elongation (50 mm, annealed)
>=40%
Not specified
Hardness (annealed, max)
212 HBS
Not specified
Tensile Strength (annealed)
>=590 MPa
Not specified
Yield Strength (0.2% proof, annealed)
>=220 MPa
Not specified
Typical Applications
IS 6911 X10Cr17Ni7
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
EN 10088-1 X5CrNi17-7
Not documented
Key Differences
EN 10088-1 X5CrNi17-7 specifies N which is not specified for IS 6911 X10Cr17Ni7.
Can IS 6911 X10Cr17Ni7 Be Substituted With EN 10088-1 X5CrNi17-7?
IS 6911 X10Cr17Ni7 and EN 10088-1 X5CrNi17-7 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X5CrNi17-7 is often considered as a substitute for IS 6911 X10Cr17Ni7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 6911 X10Cr17Ni7 and EN 10088-1 X5CrNi17-7?
EN 10088-1 X5CrNi17-7 specifies N which is not specified for IS 6911 X10Cr17Ni7.
Can IS 6911 X10Cr17Ni7 be substituted with EN 10088-1 X5CrNi17-7?
IS 6911 X10Cr17Ni7 and EN 10088-1 X5CrNi17-7 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X5CrNi17-7 is often considered as a substitute for IS 6911 X10Cr17Ni7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.