IS 6911 X15Cr16Ni2 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6911 X15Cr16Ni2 (IS 6911:1992) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X15Cr16Ni2 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. IS 6911 X15Cr16Ni2 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 6911 X15Cr16Ni2 vs GOST 5632 06Kh23N28 is a 63.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6911 X15Cr16Ni2:
ASTM A959 205 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
63.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6911 X15Cr16Ni2 GOST 5632 06Kh23N28
Standard IS 6911:1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.10-0.20 ≤0.06
Cr (%) 15.0-17.0 22.0–25.0
Mn (%) <=1.0 ≤2.00
Ni (%) 1.25-2.50 26.0–29.0
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.0 ≤0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X15Cr16Ni2 GOST 5632 06Kh23N28
Elongation (50 mm, annealed) >=10% Not specified
Hardness (annealed, max) 262 HBS Not specified
Tensile Strength (annealed) >=830 MPa Not specified
Yield Strength (0.2% proof, annealed) >=640 MPa Not specified
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
IS 6911 X15Cr16Ni2
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can IS 6911 X15Cr16Ni2 Be Substituted With GOST 5632 06Kh23N28?
IS 6911 X15Cr16Ni2 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6911 X15Cr16Ni2
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
IS 6911 X15Cr16Ni2
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X15Cr16Ni2 and GOST 5632 06Kh23N28?
IS 6911 X15Cr16Ni2 specifies P, S which are not specified for GOST 5632 06Kh23N28.
Can IS 6911 X15Cr16Ni2 be substituted with GOST 5632 06Kh23N28?
IS 6911 X15Cr16Ni2 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.