IS 6911 X20Cr25Ni20 vs GOST 5632 12Kh13

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6911 X20Cr25Ni20 (IS 6911:1992) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X20Cr25Ni20 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery. IS 6911 X20Cr25Ni20 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 6911 X20Cr25Ni20 vs GOST 5632 12Kh13 is a 64.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6911 X20Cr25Ni20:
EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
64.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6911 X20Cr25Ni20 GOST 5632 12Kh13
Standard IS 6911:1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.25 0.09–0.15
Cr (%) 24.0-26.0 12.0–14.0
Mn (%) <=2.0 ≤0.80
Ni (%) 18.0-21.0 ≤0.60
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=2.5 ≤0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X20Cr25Ni20 GOST 5632 12Kh13
Bend Test (180 deg) Not required Not specified
Elongation (50 mm, annealed) >=40% Not specified
Hardness (annealed, max) 217 HBS, 95 HRB Not specified
Tensile Strength (annealed) >=490 MPa Not specified
Yield Strength (0.2% proof, annealed) >=210 MPa Not specified
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 6911 X20Cr25Ni20
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
Can IS 6911 X20Cr25Ni20 Be Substituted With GOST 5632 12Kh13?
IS 6911 X20Cr25Ni20 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6911 X20Cr25Ni20
No active listings currently.
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 6911 X20Cr25Ni20
0 active listings and RFQs →
GOST 5632 12Kh13
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X20Cr25Ni20 and GOST 5632 12Kh13?
IS 6911 X20Cr25Ni20 specifies P, S which are not specified for GOST 5632 12Kh13.
Can IS 6911 X20Cr25Ni20 be substituted with GOST 5632 12Kh13?
IS 6911 X20Cr25Ni20 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.