IS 6911 X30Cr13 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 6911 X30Cr13 (IS 6911:1992) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 6911 X30Cr13 is typically used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 6911 X30Cr13 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6911 X30Cr13 vs EN 10088-1 1.4006 is a 68.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 6911 X30Cr13:
EN 10088-1 1.4845 GOST 5632 08X18H10 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
68.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 6911 X30Cr13 EN 10088-1 1.4006
Standard IS 6911:1992 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.26-0.35 0.08–0.15
Cr (%) 12.0-14.0 11.5–13.5
Mn (%) <=1.0 ≤1.50
Ni (%) <=1.0 ≤0.75
P (%) <=0.040 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.0 ≤1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6911 X30Cr13 EN 10088-1 1.4006
Elongation (50 mm, annealed) >=11% Not specified
Hardness (annealed, max) 235 HBS Not specified
Hardness (quenched and tempered, min) 500 HV, 49 HRC Not specified
Tensile Strength (annealed) >=780 MPa Not specified
Yield Strength (0.2% proof, annealed) >=590 MPa Not specified
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
IS 6911 X30Cr13
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 6911 X30Cr13 Be Substituted With EN 10088-1 1.4006?
IS 6911 X30Cr13 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 6911 X30Cr13
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 6911 X30Cr13
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6911 X30Cr13 and EN 10088-1 1.4006?
IS 6911 X30Cr13 specifies P, S which are not specified for EN 10088-1 1.4006.
Can IS 6911 X30Cr13 be substituted with EN 10088-1 1.4006?
IS 6911 X30Cr13 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.