Strong Match — 88.2% match
based on chemical composition and mechanical property overlap.
JIS G3506 SWRH82B (JIS G3506:2004) and SAE J403 1084 (SAE J403:2009) are both steel grades.
Both fall under the Carbon Steel category.
JIS G3506 SWRH82B is typically used for high-carbon hard-drawn steel wire rod (sw-c class, 0.80-0.85% c); used for hard-drawn steel wire, oil-tempered wire, prestressed concrete (pc) wire/strand, galvanized wire strands, wire rope, springs, tire bead wire, while SAE J403 1084 is commonly used for chemistry-only grade; product scope as listed in the composition notes.
JIS G3506 SWRH82B is defined under Japanese Industrial Standards (JIS), originating from Japan, while SAE J403 1084 is defined under SAE International, originating from United States.
As per chemical composition, JIS G3506 SWRH82B vs SAE J403 1084 is a 88.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 88.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
JIS G3506 SWRH82B
High-carbon hard-drawn steel wire rod (SW-C class, 0.80-0.85% C); used for hard-drawn steel wire, oil-tempered wire, prestressed concrete (PC) wire/strand, galvanized wire strands, wire rope, springs, tire bead wire
SAE J403 1084
Chemistry-only grade; product scope as listed in the composition notes
Key Differences
JIS G3506 SWRH82B specifies Si which is not specified for SAE J403 1084.
Can JIS G3506 SWRH82B Be Substituted With SAE J403 1084?
JIS G3506 SWRH82B and SAE J403 1084 overlap closely enough on chemistry and mechanical properties that SAE J403 1084 is often considered as a substitute for JIS G3506 SWRH82B in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G3506 SWRH82B and SAE J403 1084?
JIS G3506 SWRH82B specifies Si which is not specified for SAE J403 1084.
Can JIS G3506 SWRH82B be substituted with SAE J403 1084?
JIS G3506 SWRH82B and SAE J403 1084 overlap closely enough on chemistry and mechanical properties that SAE J403 1084 is often considered as a substitute for JIS G3506 SWRH82B in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.