JIS G4051 S22C vs BS 970 (Part 3) 070M55

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4051 S22C (JIS G4051:2009) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. JIS G4051 S22C is typically used for lightly stressed components, welded structures, while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. JIS G4051 S22C is defined under Japanese Industrial Standards (JIS), originating from Japan, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, JIS G4051 S22C vs BS 970 (Part 3) 070M55 is a 82.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4051 S22C:
BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
82.8%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4051 S22C BS 970 (Part 3) 070M55
Standard JIS G4051:2009 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.20-0.25 0.50-0.60
Si (%) 0.15-0.35 0.10-0.40
Mn (%) 0.30-0.60 0.50-0.90
S (%) <=0.035 <=0.05
P (%) <=0.030 <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4051 S22C BS 970 (Part 3) 070M55
Tensile Strength >=440 MPa Not specified
Elongation >=21% Not specified
Typical Applications
JIS G4051 S22C
Lightly stressed components, welded structures
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Can JIS G4051 S22C Be Substituted With BS 970 (Part 3) 070M55?
JIS G4051 S22C and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4051 S22C
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5000–6000 mm (196.85–236.22 in)
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
JIS G4051 S22C
2 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4051 S22C and BS 970 (Part 3) 070M55?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4051 S22C be substituted with BS 970 (Part 3) 070M55?
JIS G4051 S22C and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.