JIS G4103 SNCM420 vs SAE J404 4320

Strong Match — 86.2% match based on chemical composition and mechanical property overlap.

JIS G4103 SNCM420 (JIS G4103:1979) and SAE J404 4320 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. JIS G4103 SNCM420 is typically used for used in automotive gears, transmission parts, shafts, pinions, camshafts, and industrial equipment., while SAE J404 4320 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. JIS G4103 SNCM420 is defined under Japanese Industrial Standards (JIS), originating from Japan, while SAE J404 4320 is defined under SAE International, originating from United States.

As per chemical composition, JIS G4103 SNCM420 vs SAE J404 4320 is a 86.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.2%.

Frequently Compared With JIS G4103 SNCM420:
UNI 11234 100Cr6 GOST 4543 12HN3A NF A35-565 100C6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
86.2%
MECHANICAL MATCH
No shared data
OVERALL
86.2%
Specifications
Property JIS G4103 SNCM420 SAE J404 4320
Standard JIS G4103:1979 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.17-0.23 0.17-0.22
Si (%) 0.15-0.35 0.15-0.35
Mn (%) 0.40-0.70 0.45-0.65
P (%) 0.030 max <=0.030
S (%) 0.030 max <=0.040
Ni (%) 1.50-2.00 1.65-2.00
Cr (%) 0.40-0.80 0.40-0.60
Mo (%) 0.15-0.30 0.20-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4103 SNCM420 SAE J404 4320
Tensile Strength 780-930 MPa Not specified
Yield Strength 590 MPa min Not specified
Elongation 14% min Not specified
Hardness 217-269 HB Not specified
Typical Applications
JIS G4103 SNCM420
Used in automotive gears, transmission parts, shafts, pinions, camshafts, and industrial equipment.
SAE J404 4320
Chemistry-only alloy steel grade; see the composition notes for product scope
Can JIS G4103 SNCM420 Be Substituted With SAE J404 4320?
JIS G4103 SNCM420 and SAE J404 4320 overlap closely enough on chemistry and mechanical properties that SAE J404 4320 is often considered as a substitute for JIS G4103 SNCM420 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
JIS G4103 SNCM420
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5900–6000 mm (232.28–236.22 in)
SAE J404 4320
No active listings currently.
On M-EX Right Now
JIS G4103 SNCM420
2 active listings and RFQs →
SAE J404 4320
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4103 SNCM420 and SAE J404 4320?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4103 SNCM420 be substituted with SAE J404 4320?
JIS G4103 SNCM420 and SAE J404 4320 overlap closely enough on chemistry and mechanical properties that SAE J404 4320 is often considered as a substitute for JIS G4103 SNCM420 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.