Post Stock Login Register

JIS G4104 SCr420 vs SAE J404 5130

Close Alternative — 83.5% match based on chemical composition and mechanical property overlap.

JIS G4104 SCr420 (JIS G 4104:1979) and SAE J404 5130 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. JIS G4104 SCr420 is typically used for case hardened gears, shafts, cams, while SAE J404 5130 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. JIS G4104 SCr420 is defined under Japanese Industrial Standards (JIS), originating from Japan, while SAE J404 5130 is defined under SAE International, originating from United States.

As per chemical composition, JIS G4104 SCr420 vs SAE J404 5130 is a 83.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.5%.

Frequently Compared With JIS G4104 SCr420:
GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
83.5%
MECHANICAL MATCH
No shared data
OVERALL
83.5%
Specifications
Property JIS G4104 SCr420 SAE J404 5130
Standard JIS G 4104:1979 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.18–0.23 0.28-0.33
Si (%) 0.15–0.35 0.15-0.35
Mn (%) 0.60–0.90 0.70-0.90
Cr (%) 0.90–1.20 0.80-1.10
P (%) ≤0.030 <=0.030
S (%) ≤0.030 <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4104 SCr420 SAE J404 5130
Tensile Strength ≥830 MPa Not specified
Case Hardness HRC 58–62 Not specified
Core Hardness HB 235–293 Not specified
Typical Applications
JIS G4104 SCr420
Case hardened gears, shafts, cams
SAE J404 5130
Chemistry-only alloy steel grade; see the composition notes for product scope
Can JIS G4104 SCr420 Be Substituted With SAE J404 5130?
JIS G4104 SCr420 and SAE J404 5130 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
JIS G4104 SCr420
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5300–5600 mm (208.66–220.47 in)
SAE J404 5130
No active listings currently.
On M-EX Right Now
JIS G4104 SCr420
2 active listings and RFQs →
SAE J404 5130
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4104 SCr420 and SAE J404 5130?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4104 SCr420 be substituted with SAE J404 5130?
JIS G4104 SCr420 and SAE J404 5130 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.