Minimal Match — 51.6% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS301L (JIS G4304:2021) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS301L is typically used for hot-rolled stainless steel plates and strips, while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware.
JIS G4304 SUS301L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.
As per chemical composition, JIS G4304 SUS301L vs EN 10088-1 1.4301 is a 64.9% match.
As per mechanical properties, the match is 25%.
Combined, this makes them a minimal match overall at 51.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS301L
EN 10088-1 1.4301
Tensile Strength
>=550 MPa
≥520 MPa
Yield Strength
>=215 MPa
≥210 MPa
Elongation
>=45%
≥45%
Hardness
<=207 HB
≤215 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4304 SUS301L
Hot-rolled stainless steel plates and strips
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
JIS G4304 SUS301L specifies N which is not specified for EN 10088-1 1.4301.
Can JIS G4304 SUS301L Be Substituted With EN 10088-1 1.4301?
JIS G4304 SUS301L and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4304 SUS301L and EN 10088-1 1.4301?
JIS G4304 SUS301L specifies N which is not specified for EN 10088-1 1.4301.
Can JIS G4304 SUS301L be substituted with EN 10088-1 1.4301?
JIS G4304 SUS301L and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.