JIS G4304 SUS304J2 vs GB/T 3280 06Cr19Ni10

Related Material — 57.9% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS304J2 (JIS G4304:2021) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS304J2 is typically used for hot-rolled stainless steel plates and strips, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. JIS G4304 SUS304J2 is defined under Japanese Industrial Standards (JIS), originating from Japan, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, JIS G4304 SUS304J2 vs GB/T 3280 06Cr19Ni10 is a 74.4% match. As per mechanical properties, the match is 25%. Combined, this makes them a related material overall at 57.9%.

Frequently Compared With JIS G4304 SUS304J2:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
74.4%
MECHANICAL MATCH
25%
OVERALL
57.9%
Specifications
Property JIS G4304 SUS304J2 GB/T 3280 06Cr19Ni10
Standard JIS G4304:2021 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08 max
Si (%) <=1.70 1.00 max
Mn (%) 3.00-5.00 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.030 0.030 max
Ni (%) 6.00-9.00 8.00-11.00
Cr (%) 15.00-18.00 18.00-20.00
Cu (%) 1.00-3.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS304J2 GB/T 3280 06Cr19Ni10
Tensile Strength >=450 MPa 520-720 MPa
Yield Strength >=155 MPa 205-310 MPa
Elongation >=40% 40-60%
Hardness <=187 HB 187 HB max
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS304J2
Hot-rolled stainless steel plates and strips
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can JIS G4304 SUS304J2 Be Substituted With GB/T 3280 06Cr19Ni10?
JIS G4304 SUS304J2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4304 SUS304J2
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
JIS G4304 SUS304J2
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS304J2 and GB/T 3280 06Cr19Ni10?
JIS G4304 SUS304J2 specifies Cu which is not specified for GB/T 3280 06Cr19Ni10.
Can JIS G4304 SUS304J2 be substituted with GB/T 3280 06Cr19Ni10?
JIS G4304 SUS304J2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.