JIS G4304 SUS304N2 vs EN 10088-1 X5CrNi18-10

Close Alternative — 82.5% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS304N2 (JIS G4304:2021) and EN 10088-1 X5CrNi18-10 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS304N2 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4304 SUS304N2 vs EN 10088-1 X5CrNi18-10 is a 82.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.5%.

Frequently Compared With JIS G4304 SUS304N2:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
82.5%
MECHANICAL MATCH
No shared data
OVERALL
82.5%
Specifications
Property JIS G4304 SUS304N2 EN 10088-1 X5CrNi18-10
Standard JIS G4304:2021 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.07
Si (%) <=1.00 <=1.00
Mn (%) <=2.50 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Ni (%) 7.50-10.50 8.0-10.5
Cr (%) 18.00-20.00 17.5-19.5
N (%) 0.15-0.30 <=0.10
Nb (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS304N2 EN 10088-1 X5CrNi18-10
Tensile Strength >=690 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=35% Not specified
Hardness <=248 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS304N2
Hot-rolled stainless steel plates and strips
EN 10088-1 X5CrNi18-10
Not documented
Key Differences
Can JIS G4304 SUS304N2 Be Substituted With EN 10088-1 X5CrNi18-10?
JIS G4304 SUS304N2 and EN 10088-1 X5CrNi18-10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS304N2
0 active listings and RFQs →
EN 10088-1 X5CrNi18-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS304N2 and EN 10088-1 X5CrNi18-10?
JIS G4304 SUS304N2 specifies Nb which is not specified for EN 10088-1 X5CrNi18-10.
Can JIS G4304 SUS304N2 be substituted with EN 10088-1 X5CrNi18-10?
JIS G4304 SUS304N2 and EN 10088-1 X5CrNi18-10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.