Post Stock Login Register

JIS G4304 SUS315J2 vs ASTM A959 316Ti

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS315J2 (JIS G4304:2021) and ASTM A959 316Ti (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS315J2 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 316Ti is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS315J2 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 316Ti is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS315J2 vs ASTM A959 316Ti is a 72% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4304 SUS315J2:
IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
72%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4304 SUS315J2 ASTM A959 316Ti
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) 2.50-4.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 11.00-14.00 10.0-14.0
Cr (%) 17.00-20.50 16.0-18.0
Mo (%) 0.50-1.50 2.00-3.00
Cu (%) 0.50-3.50 Not specified
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS315J2 ASTM A959 316Ti
Tensile Strength >=520 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=40% Not specified
Hardness <=187 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS315J2
Hot-rolled stainless steel plates and strips
ASTM A959 316Ti
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS315J2 Be Substituted With ASTM A959 316Ti?
JIS G4304 SUS315J2 and ASTM A959 316Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4304 SUS315J2
0 active listings and RFQs →
ASTM A959 316Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS315J2 and ASTM A959 316Ti?
JIS G4304 SUS315J2 specifies Cu which is not specified for ASTM A959 316Ti. ASTM A959 316Ti specifies N which is not specified for JIS G4304 SUS315J2.
Can JIS G4304 SUS315J2 be substituted with ASTM A959 316Ti?
JIS G4304 SUS315J2 and ASTM A959 316Ti share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.