Strong Match — 100% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS316L (JIS G4304:2021) and JIS G4305 SUS316L (JIS G4305:2012) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS316L is typically used for hot-rolled stainless steel plates and strips, while JIS G4305 SUS316L is commonly used for cold-rolled stainless steel plates, sheet and strip.
JIS G4304 SUS316L is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4305 SUS316L is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4304 SUS316L vs JIS G4305 SUS316L is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS316L
JIS G4305 SUS316L
Tensile Strength
>=480 MPa
>=480 MPa
Yield Strength
>=175 MPa
>=175 MPa
Elongation
>=40%
>=40%
Hardness
<=187 HB
<=187 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
JIS G4304 SUS316L
Hot-rolled stainless steel plates and strips
JIS G4305 SUS316L
Cold-rolled stainless steel plates, sheet and strip
Can JIS G4304 SUS316L Be Substituted With JIS G4305 SUS316L?
JIS G4304 SUS316L and JIS G4305 SUS316L overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS316L is often considered as a substitute for JIS G4304 SUS316L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4304 SUS316L and JIS G4305 SUS316L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS316L be substituted with JIS G4305 SUS316L?
JIS G4304 SUS316L and JIS G4305 SUS316L overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS316L is often considered as a substitute for JIS G4304 SUS316L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.