JIS G4304 SUS317J1 vs ASTM A959 317LM

Close Alternative — 78.1% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS317J1 (JIS G4304:2021) and ASTM A959 317LM (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS317J1 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 317LM is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS317J1 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 317LM is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS317J1 vs ASTM A959 317LM is a 78.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 78.1%.

Frequently Compared With JIS G4304 SUS317J1:
ASTM A959 .- IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
78.1%
MECHANICAL MATCH
No shared data
OVERALL
78.1%
Specifications
Property JIS G4304 SUS317J1 ASTM A959 317LM
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.040 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.50 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 15.00-17.00 13.5-17.5
Cr (%) 16.00-19.00 18.0-20.0
Mo (%) 4.00-6.00 4.0-5.0
N (%) Not specified <=0.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS317J1 ASTM A959 317LM
Tensile Strength >=480 MPa Not specified
Yield Strength >=175 MPa Not specified
Elongation >=40% Not specified
Hardness <=187 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS317J1
Hot-rolled stainless steel plates and strips
ASTM A959 317LM
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS317J1 Be Substituted With ASTM A959 317LM?
JIS G4304 SUS317J1 and ASTM A959 317LM are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS317J1
0 active listings and RFQs →
ASTM A959 317LM
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS317J1 and ASTM A959 317LM?
ASTM A959 317LM specifies N which is not specified for JIS G4304 SUS317J1.
Can JIS G4304 SUS317J1 be substituted with ASTM A959 317LM?
JIS G4304 SUS317J1 and ASTM A959 317LM are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.