Close Alternative — 82.6% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS317J1 (JIS G4304:2021) and JIS G4304 SUS317L (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS317J1 is typically used for hot-rolled stainless steel plates and strips, while JIS G4304 SUS317L is commonly used for hot-rolled stainless steel plates and strips.
JIS G4304 SUS317J1 is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4304 SUS317L is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4304 SUS317J1 vs JIS G4304 SUS317L is a 73.9% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a close alternative overall at 82.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS317J1
JIS G4304 SUS317L
Tensile Strength
>=480 MPa
>=480 MPa
Yield Strength
>=175 MPa
>=175 MPa
Elongation
>=40%
>=40%
Hardness
<=187 HB
<=187 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
JIS G4304 SUS317J1
Hot-rolled stainless steel plates and strips
JIS G4304 SUS317L
Hot-rolled stainless steel plates and strips
Can JIS G4304 SUS317J1 Be Substituted With JIS G4304 SUS317L?
JIS G4304 SUS317J1 and JIS G4304 SUS317L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between JIS G4304 SUS317J1 and JIS G4304 SUS317L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS317J1 be substituted with JIS G4304 SUS317L?
JIS G4304 SUS317J1 and JIS G4304 SUS317L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.