JIS G4304 SUS317J2 vs BS 970 (Part 1) 316S31

Related Material — 68.7% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS317J2 (JIS G4304:2021) and BS 970 (Part 1) 316S31 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS317J2 is typically used for hot-rolled stainless steel plates and strips, while BS 970 (Part 1) 316S31 is commonly used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition).. JIS G4304 SUS317J2 is defined under Japanese Industrial Standards (JIS), originating from Japan, while BS 970 (Part 1) 316S31 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, JIS G4304 SUS317J2 vs BS 970 (Part 1) 316S31 is a 68.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68.7%.

Frequently Compared With JIS G4304 SUS317J2:
ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
68.7%
MECHANICAL MATCH
No shared data
OVERALL
68.7%
Specifications
Property JIS G4304 SUS317J2 BS 970 (Part 1) 316S31
Standard JIS G4304:2021 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.07
Si (%) <=1.50 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 12.00-16.00 10.5-13.5
Cr (%) 23.00-26.00 16.5-18.5
Mo (%) 0.50-1.20 2.00-2.50
N (%) 0.25-0.40 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS317J2 BS 970 (Part 1) 316S31
Tensile Strength >=690 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=40% Not specified
Hardness <=250 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS317J2
Hot-rolled stainless steel plates and strips
BS 970 (Part 1) 316S31
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Key Differences
Can JIS G4304 SUS317J2 Be Substituted With BS 970 (Part 1) 316S31?
JIS G4304 SUS317J2 and BS 970 (Part 1) 316S31 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4304 SUS317J2
0 active listings and RFQs →
BS 970 (Part 1) 316S31
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS317J2 and BS 970 (Part 1) 316S31?
JIS G4304 SUS317J2 specifies N which is not specified for BS 970 (Part 1) 316S31.
Can JIS G4304 SUS317J2 be substituted with BS 970 (Part 1) 316S31?
JIS G4304 SUS317J2 and BS 970 (Part 1) 316S31 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.