JIS G4304 SUS327L1 vs EN 10088-1 X2CrNiMoCuN25-6-3

Strong Match — 86.7% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS327L1 (JIS G4304:2021) and EN 10088-1 X2CrNiMoCuN25-6-3 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS327L1 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X2CrNiMoCuN25-6-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4304 SUS327L1 vs EN 10088-1 X2CrNiMoCuN25-6-3 is a 86.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.7%.

Frequently Compared With JIS G4304 SUS327L1:
ASTM A959 2507 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
86.7%
MECHANICAL MATCH
No shared data
OVERALL
86.7%
Specifications
Property JIS G4304 SUS327L1 EN 10088-1 X2CrNiMoCuN25-6-3
Standard JIS G4304:2021 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.80 <=0.70
Mn (%) <=1.20 <=2.00
P (%) <=0.035 <=0.035
S (%) <=0.020 <=0.015
Ni (%) 6.00-8.00 6.0-8.0
Cr (%) 24.00-26.00 24.0-26.0
Mo (%) 3.00-5.00 3.00-4.0
Cu (%) <=0.50 1.00-2.50
N (%) 0.24-0.32 0.20-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS327L1 EN 10088-1 X2CrNiMoCuN25-6-3
Tensile Strength >=795 MPa Not specified
Yield Strength >=550 MPa Not specified
Elongation >=15% Not specified
Hardness <=310 HB Not specified
Condition Solution heat treated plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS327L1
Hot-rolled stainless steel plates and strips
EN 10088-1 X2CrNiMoCuN25-6-3
Not documented
Can JIS G4304 SUS327L1 Be Substituted With EN 10088-1 X2CrNiMoCuN25-6-3?
JIS G4304 SUS327L1 and EN 10088-1 X2CrNiMoCuN25-6-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuN25-6-3 is often considered as a substitute for JIS G4304 SUS327L1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4304 SUS327L1
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuN25-6-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS327L1 and EN 10088-1 X2CrNiMoCuN25-6-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS327L1 be substituted with EN 10088-1 X2CrNiMoCuN25-6-3?
JIS G4304 SUS327L1 and EN 10088-1 X2CrNiMoCuN25-6-3 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoCuN25-6-3 is often considered as a substitute for JIS G4304 SUS327L1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.