JIS G4304 SUS329J4L vs EN 10088-1 X2CrNiMoN25-7-4

Close Alternative — 83% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS329J4L (JIS G4304:2021) and EN 10088-1 X2CrNiMoN25-7-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS329J4L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4304 SUS329J4L vs EN 10088-1 X2CrNiMoN25-7-4 is a 83% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83%.

Frequently Compared With JIS G4304 SUS329J4L:
ASTM A959 .- ASTM A959 25-4-4 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
83%
MECHANICAL MATCH
No shared data
OVERALL
83%
Specifications
Property JIS G4304 SUS329J4L EN 10088-1 X2CrNiMoN25-7-4
Standard JIS G4304:2021 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.50 <=2.00
P (%) <=0.040 <=0.035
S (%) <=0.030 <=0.015
Ni (%) 5.50-7.50 6.0-8.0
Cr (%) 24.00-26.00 24.0-26.0
Mo (%) 2.50-3.50 3.0-4.5
N (%) 0.08-0.30 0.24-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS329J4L EN 10088-1 X2CrNiMoN25-7-4
Tensile Strength >=620 MPa Not specified
Yield Strength >=450 MPa Not specified
Elongation >=18% Not specified
Hardness <=302 HB Not specified
Condition Solution heat treated plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS329J4L
Hot-rolled stainless steel plates and strips
EN 10088-1 X2CrNiMoN25-7-4
Not documented
Can JIS G4304 SUS329J4L Be Substituted With EN 10088-1 X2CrNiMoN25-7-4?
JIS G4304 SUS329J4L and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS329J4L
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS329J4L and EN 10088-1 X2CrNiMoN25-7-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS329J4L be substituted with EN 10088-1 X2CrNiMoN25-7-4?
JIS G4304 SUS329J4L and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.